Panchdeep Metal Corp is a manufacturer and supplier of high quality of Stainless Steel 409 Shim. . We at Panchdeep are involved in the production and supply of SS 409 Shims that have found application in a wide array of industries. This is because of the excellent resistivity against corrosion they offer. The Stainless Steel 409 Shims are manufactured in a variety of different sizes in thickness. The thickness of the SS 409 Shims that we produce is available in thickness ranging from 0.05mm to 6mm (.002″ to .250″) for quick turnaround of shims.
The Stainless Steel 409 Shim from Panchdeep Metal is known to have high resistivity against corrosion and oxidation. These Shims are highly suitable for applications in high-temperature applications. They offer excellent resistance to exhaust gas and atmospheric corrosion. The Stainless Steel 409 Shims offer oxidation resistance up to temperatures up to 675°C during continuous operation and up to 815°C under intermittent conditions. The Stainless Steel 409 Shims are used in various industries for applications such as the manufacturing of Catalytic converter systems and Mufflers. They are also used in the automobile industry for the manufacturing of Automotive exhaust tubing. The Stainless Steel 409 Shims are also used for decorative purposes.
Stainless Steel 409 Shim Specifications:
|Standard||ASTM / ASME A240 / SA240|
|Width||14′ (355 MM) to 2′ (610 MM)|
|Thickness||0.05 MM thickness, 0.10 MM, 0.15 MM, 0.20 MM, 0.25 MM, 0. 30 MM, 0. 35 MM, 0.40 MM|
|Form||Decorative Round Hole, Dimpled, Square Holes, Gold Mirror Round Hole, Round Punch, Etched, Colored Shim Sheets|
|Hardness||Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.|
Chemical Properties of SS 409 Shim
|SS 409||0.08 max||2.0 max||1.00 max||0.045 max||0.030 max||17 – 19||10xC – 1.10||9 – 12||5(C+N) – 0.70 max|
Mechanical Properties of SS 409 Shim
|Density||Melting Point||Tensile Strength||Yield Strength (0.2%Offset)||Elongation|
|8.0 g/cm3||1457 °C (2650 °F)||Psi – 75000 , MPa – 515||Psi – 30000 , MPa – 205||35 %|