Panchdeep metal process and stocks SS 3CR12 Plate in different specification, grades, thickness, dimensions, and shapes. These plates are ferritic utility SS grade that provides resistance to corrosion and heat. Plates have most benefits expected from other SS grade plates. Additional advantages are weldability and formability prominent for engineering applications. 3CR12 SS plates are cost advantage compared to other resisting plate grades. In service, this grade SS plates provides saving and maintenance and provide improved productivity within a low machining costs
This grade of plates is fully austenitic at elevates temperatures. Stainless Steel 3CR12 plates are both magnetic and non-magnetic in nature. Its fine grain structure makes it worth for welding and other fabrication application. Typically, plates offer excellent performance and economy. These plates are drawn from hot and cold rolling mills. For extra hardening, plates are treated with heat treatment process, also finished by the matte finish, hairline, sandblasting and BA finish.
Steel 3CR12 Plate is processed with different quality tests under the professionals. The test includes- hardness, mechanical test, flattening, flaring test, destructive and non-destructive test, and visual inspection test. Final testing is performed by the third parties so that product is reached at top-notch quality. Along with product producers attach some quality proof documentations like- commercial invoice, packaging details, specification guide, raw material report, lab reports.
These plates are delivered in the standards packing of wooden box/ crates/ pallets or bundles with plastic wrap. It ensures none of any product gets damaged while exporting it to global clients. Buy them for long-lasting fabrication application.
Stainless Steel 3CR12 Plates Specifications:
|Specifications||ASTM A240, ASME SA240|
|Standard||JIS, ASTM, AISI, GB, EN, DIN|
|Surface||2B, 2D, BA, NO.4, NO.8, 8K, Mirror, Checkered, Embossed, Hair Line, Sand Blast, Brush, Etching|
|Finish||Cold rolled, Hot rolled|
|Thickness||0.40mm – 6.00mm|
Chemical Properties of SS 3CR12 Plates
|C||Si ≤||Mn ≤||P ≤||S ≤||N ≤||Cr||Ni|
|≤0.030||1.00||1.50||0.040||0.015||0.030||10.5 – 12.5||0.30 – 1.00|
Mechanical Properties of SS 3CR12 Plates
|Tensile Strength||Yield Strength||Elongation (%)||Reduction of area (%)||Charpy(Akv)||Hardness|
|450-600MPa||260MPa min||20||53||J min||200 max|