SS X2CrNi12 Plate is one of the most demanding and widely used products that are used in various applications and industries. It is widely used in railway sectors for manufacturing different railway parts. Panchdeep metal is one of the leading manufacturers and suppliers of stainless steel plates used widely due to their excellent features and properties. We make use of superior quality material and latest machines for manufacturing. Each and every material used for manufacturing these plates is well inspected and tested in accordance with the industrial norms and regulations.
There are various features that make these plates different from other grades of the plate. Such as rust resistant, durability, high tensile strength, corrosion resistant, well-built construction, dimensional accuracy and more. These plates are manufactured using hot rolled and cold rolled processes. We even provide our customers with varied shapes and sizes of plates as per their demand and application requirement. However, if we talk about the testing process, we conduct different tests to check the quality of these plates.
The tests include flaring test, radiography test, flattening test, third-party inspection, hardness test, PMI test, IBR test and more. All these tests are done under the guidance and regulations of quality experts and inspection agencies under different parameters. For all these tests, different test certificates are approved that are offered to customers and clients, proving product quality. To keep the Steel X2CrNi12 Plate protected and avoid damages the plates are packed in the high quality of packaging material.
Hence, if you are thinking of buying X2CrNi12 Plate then buy it from Panchdeep metal only.
Stainless Steel X2CrNi12 Plates Specifications:
|Specifications||ASTM A240, ASME SA240|
|Standard||JIS, ASTM, AISI, GB, EN, DIN|
|Surface||2B, 2D, BA, NO.4, NO.8, 8K, Mirror, Checkered, Embossed, Hair Line, Sand Blast, Brush, Etching|
|Finish||Cold rolled, Hot rolled|
|Thickness||0.40mm – 6.00mm|
Chemical Properties of SS X2CrNi12 Plates
|C||Si ≤||Mn ≤||P ≤||S ≤||N ≤||Cr||Ni|
|≤0.030||1.00||1.50||0.040||0.015||0.030||10.5 – 12.5||0.30 – 1.00|
Mechanical Properties of SS X2CrNi12 Plates
|Tensile Strength||Yield Strength||Elongation (%)||Reduction of area (%)||Charpy(Akv)||Hardness|
|450-600MPa||260MPa min||20||53||J min||200 max|