The AISI/SS 439 Plate is ferritic stainless steel and it is furnished in the annealed condition. These plates are widely used in applications that require high corrosion and oxidation resistance. This grade contains proper surface finish and brightness. This grade contains chromium and nickel alloy that is usually used for pressure vessels and other general applications. These plates are accessible in different sizes and shapes. These are designed as per both national and international standards. These plates are extremely long lasting and can easily fit without any trouble.
• Good corrosion and oxidation resistance
• Good formability and weldability
• Longer service life
• Precise dimensions
• Excellent resistance to stress corrosion cracking
Quality control measurement-
These plates are tested under various quality measurement tests to ensure product quality. These entire tests are done under the guidance of experts to meet the products in terms of best quality.
• Intergranular test
• Positive material identification test
• Flaring and flattering test
• Micro and macro test
• Third party inspection and more
Marking and Packaging-
The marking is done by the company and it will include grade no, item no, lot no etc. To deliver damage free products without any flaw the standard packing method is used.
• Wooden case or box
• Plywood case or crates
Panchdeep metal offers all kind of stainless steel plate in affordable rates. These plates are made as per buyer requirement. It is useful for industrial applications prospects. If you want to buy the quality product then must visit the shop and get quality products.
Stainless Steel 439 Plates Specifications:
|Specifications||ASTM A240, ASME SA240|
|Standard||JIS, ASTM, AISI, GB, EN, DIN|
|Surface||2B, 2D, BA, NO.4, NO.8, 8K, Mirror, Checkered, Embossed, Hair Line, Sand Blast, Brush, Etching|
|Finish||Cold rolled, Hot rolled|
|Thickness||0.40mm – 6.00mm|
Chemical Properties of SS 439 Plates
Mechanical Properties of SS 439 Plates
|Tensile strength (annealed)||438 MPa||63500 psi|
|Yield strength (annealed/ @strain 0.200 %)||263 MPa||38100 psi|
|Modulus of elasticity||GPa||ksi|
|Poisson’s ratio||0.270 – 0.290||0.270 – 0.290|
|Elongation at break (In 2″, 50% cold worked)||2.80%||2.80%|
|Hardness, Rockwell B (annealed)||72.9||72.9|