The AISI/SS 316Ti Coils is the best kind of stainless steel alloy coils. It is basically made of Lower carbon steel alloy. It is not having much of the carbon percentage than the other stainless steel and Due to this property, it if slow at hardening. Thus it becomes easy for the manufacturers to work on the stainless steel coils and to reformulate them. They are basically thermally non-hardenable. These coils are made of Austenitic stainless steel and thus are having good forming and welding properties.
This grade of stainless steel alloys is having chromium and nickel in it along with molybdenum. Thus they are having good resistance property against corrosion. They are having corrosion resistance due to oxidation and reducing agents and to the atmospheric and weathering conditions. They are also having good resistance to the toxic gases, steam, and some mild and strong chemicals. This makes these coils to be the demand of all kind of industrial work.
The stainless steel coils of 316Ti grade are having good resistance towards heat. They are easy at forming and machining at high temperature. As they are slow at hardening they provide more time to its manufacturers and thus they are having excellent flawless and smooth finish.
The Panchdeep metal is the leading traders of the AISI/SS 316Ti Coil. This company is not only concerned about the construction of the coils but also on its supplying and packaging. They also provide the customized sizes and packaging of the stainless steel coils at very cheaper and very reasonable rates.
Stainless Steel 316TI Coils Specifications:
|Specifications||ASTM A240, ASME SA240|
|Standard||JIS, ASTM, AISI, GB, EN, DIN|
|Surface||2B, BA, HL, No. 4, Mirror etc.|
|Finish||Cold rolled, Hot rolled|
|Size||1000mm, 1219mm, 1250mm, 1500mm, 1524mm, 2000mm|
Chemical Properties of SS 316TI Coils
|SS 316Ti||0.08 max||2.0 max||0.75 max||0.045 max||0.030 max||16.00 – 18.00||2.00 – 3.00||10.00 – 14.00||68.395 min|
Mechanical Properties of SS 316TI Coils
|Density||Melting Point||Tensile Strength||Yield Strength (0.2%Offset)||Elongation|
|8.0 g/cm3||1399 °C (2550 °F)||Psi – 75000 , MPa – 515||Psi – 30000 , MPa – 205||35 %|