The AISI/SS 430 Coil is the best known stainless steel coils which are certified with AISI. This alloy is composed with the elements like as chromium, nickel, and manganese. This is basically non-hardenable such as it is soft in nature. These coils are thus best known for the industrial purpose and are in great demand. The Panchdeep metal is the leading manufacturers of the AISI/SS 430 Coils. They provide the best stainless steel coils which are made of 100% raw quality material.
These coils provide excellent resistance towards corrosion from oxidation and reduction. They also provide good resistance towards moisture and steam pressure. They can easily withstand to the effect of nitric and sulphuric acid. These alloys are also having great mechanical properties. They can be easily machined as they are soft in nature. They are also easy at welding even at a lower temperature.
The Panchdeep metal is the leading manufacturers of the AISI/SS 430 Coils. They are the manufacturers as well as the suppliers of the stainless steel coils. These are even tested with different kind of tests such as hardness test, flaring test, and intergranular test and also they are analyzed by the different analysis such as chemical analysis and Spectro analysis.
They are also concerned with the proper packaging of the coil. They are initially wrapped with the standard packing belt or the string and then it is overlapped with the foam warp or the bubble wrap. They are then kept in the airtight metallic and wooden boxes in considering the adverse effect of rusting.
Stainless Steel 430 Coils Specifications:
|Specifications||ASTM A240, ASME SA240|
|Standard||JIS, ASTM, AISI, GB, EN, DIN|
|Surface||2B, BA, HL, No. 4, Mirror etc.|
|Finish||Cold rolled, Hot rolled|
|Thickness||0.8 mm to 10 mm|
Chemical Properties of SS 430 Coils
|SS 430||16.00 – 18.00||0.0 – 1.00||0.0 – 1.00||0.0 – 0.08||0.0 – 0.04||0.0 – 0.02||Balance|
Mechanical Properties of SS 430 Coils
|Proof Stress||Tensile Strength||Elongation A50 mm|
|260 Min MPa||450 – 600 MPa||20 Min %|