The AISI/SS 410 Coil is the most used kind of stainless steel coils. These are made of the austenitic stainless steel alloy. This alloy consists of chromium, nickel, and manganese. The stainless steel alloys coils are the basic applications of many industries now. They are being formulated and worked in the annealed conditions. These coils are non-hardenable with the high-temperature treatment. Thus these coils are easily workable and provide excellent finish in nature.
The Panchdeep metal is the leading firm known as the best sellers of the AISI/SS 410 Coil. They prove the best kind of stainless steel coils of 410 grade at a very cheap rate. Their every product is being certified as the best equipment for the industrial purpose. The stainless steel coils thus formed are made of 100% high-quality raw material. These are tested with the following tests like Mechanical Testing, Hardness Test, Positive Material Identification –Flattening Test, PMI Testing, Micro, and Macro Test, Pitting Resistance Test, , Intergranular Corrosion (IGC) Test Flaring Test. These coils have also been undergone the analysis like Chemical Analysis and Spectro Analysis.
The AISI/SS 410 Coil is having good services in the packaging. The stainless steel coils are being packed in the standard packages. Each specific coil is being wrapped closely without any air contact. These are then wrapped with packaging string or belt so that they do not get spread. Then the coils are being packed in the bubble wrap or the foam. Then each coil is kept in the wooden or metallic boxes.
Stainless Steel 410 Coils Specifications:
|Specifications||ASTM A240, ASME SA240|
|Standard||JIS, ASTM, AISI, GB, EN, DIN|
|Surface||2B, BA, HL, No. 4, Mirror etc.|
|Finish||Cold rolled, Hot rolled|
|Size||1000mm, 1219mm, 1250mm, 1500mm, 1524mm, 2000mm|
Chemical Properties of SS 410 Coils
|SS 410||11.50 – 13.50||0.0 – 1.50||0.0 – 1.00||0.0 – 0.75||0.08 – 0.15||0.0 – 0.04||0.0 – 0.02||Balance|
Mechanical Properties of SS 410 Coils
|Tensile Strength Ksi (Mpa)||0.2% Offset Yield Strength Ksi (Mpa)||Elongation, % in 2″ (51 mm)||Hardening Response HRC||HRB|
|65 (450) – 74 (510)||30 (205) – 42 (290)||20 – 34||38-45||82-96|